Glass-fibre reinforced polyamide based (PA) technopolymer, black colour, matte finish.
Supplied assembled. The seat for housing the tube in the shank is shaped so as to prevent its rotation.
Glass-fibre reinforced polyester, black colour with high resistivity. High resistance to wear, scratches and agents.
Rear fastening with screws M10.
Two reference pins (to be fitted during assembly) guarantee a precise positioning.
Tensile stress: F2 values reported in the table are the result of breaking tests carried out with the appropriate dynamometric equipment under the test conditions shown in the figure with ambient temperature.
The following table lists the main dielectric features of the tube.
Dielectric features of the tube | |
---|---|
Volume Resistivity | 1010 ÷ 1015 [Ω *cm] |
Surface resistivity | 1010 ÷ 1013 [Ω*] (according to IEC93 standard) |
Dielectric resistivity | 8 [KV/mm] |
Comparative tracking index (CTI) | > 600 (V) |
Dielectric constant | 5 |
SCM.: intermediate shank for tube Ø30 in polyester based (PBT) technopolymer, black colour, matte finish. Suggested for tube longer than 700 mm (see table).