Technopolymer
Catalogue
|
Description
|
L
|
dH9
|
d6H
|
S
|
H
|
d2
|
h
|
h1
|
l2
|
F
[N] |
|
---|---|---|---|---|---|---|---|---|---|---|---|---|
|
|
|
|
|
|
|
|
|
|
|
|
|
32420
|
L.652/40 B-M5-C9
|
41
|
-
|
M5
|
13
|
28
|
-
|
16
|
18.5
|
-
|
2400
|
17
|
32421
|
L.652/40 B-6-C9
|
41
|
6
|
-
|
13
|
28
|
9
|
18
|
18.5
|
23
|
2500
|
16
|
32426
|
L.652/40 B-M6-C9
|
41
|
-
|
M6
|
13
|
28
|
-
|
16
|
18.5
|
-
|
2500
|
16
|
32430
|
L.652/55 B-M5-C9
|
56.5
|
-
|
M5
|
15
|
33
|
-
|
15
|
21.5
|
-
|
2400
|
28
|
32431
|
L.652/55 B-6-C9
|
56.5
|
6
|
-
|
15
|
33
|
10
|
18
|
21.5
|
27
|
3300
|
27
|
32436
|
L.652/55 B-M6-C9
|
56.5
|
-
|
M6
|
15
|
33
|
-
|
18
|
21.5
|
-
|
3300
|
27
|
32432
|
L.652/55 B-M8-C9
|
56.5
|
-
|
M8
|
15
|
33
|
-
|
20
|
21.5
|
-
|
3300
|
28
|
32441
|
L.652/67 B-6-C9
|
68.5
|
6
|
-
|
16.5
|
37
|
11
|
20
|
24.5
|
30
|
4500
|
38
|
32443
|
L.652/67 B-8-C9
|
68.5
|
8
|
-
|
16.5
|
37
|
11
|
20
|
24.5
|
30
|
4500
|
36
|
32446
|
L.652/67 B-M8-C9
|
68.5
|
-
|
M8
|
16.5
|
37
|
-
|
20
|
24.5
|
-
|
4500
|
36
|
32452
|
L.652/67 B-M10-C9
|
68.5
|
-
|
M10
|
16.5
|
37
|
-
|
20
|
24.5
|
-
|
5000
|
34
|
32451
|
L.652/80 B-6-C9
|
82
|
6
|
-
|
20
|
41.5
|
13
|
25
|
25
|
33
|
7000
|
58
|
32453
|
L.652/80 B-8-C9
|
82
|
8
|
-
|
20
|
41.5
|
13
|
25
|
25
|
33
|
7000
|
52
|
32456
|
L.652/80 B-M8-C9
|
82
|
-
|
M8
|
20
|
41.5
|
-
|
25
|
25
|
-
|
7000
|
50
|
32458
|
L.652/80 B-M10-C9
|
82
|
-
|
M10
|
20
|
41.5
|
-
|
25
|
25
|
-
|
7000
|
56
|
32460
|
L.652/80 B-M12-C9
|
82
|
-
|
M12
|
20
|
41.5
|
-
|
18
|
25
|
-
|
7000
|
62
|
32471
|
L.652/95 B-6-C9
|
94
|
6
|
-
|
21
|
46
|
13
|
25
|
28.5
|
33
|
8000
|
74
|
32476
|
L.652/95 B-M8-C9
|
94
|
-
|
M8
|
21
|
46
|
13
|
25
|
28.5
|
33
|
8000
|
72
|
32478
|
L.652/95 B-M10-C9
|
94
|
-
|
M10
|
21
|
46
|
-
|
25
|
28.5
|
-
|
8000
|
70
|
32480
|
L.652/95 B-M12-C9
|
94
|
-
|
M12
|
21
|
46
|
-
|
18
|
28.5
|
-
|
8000
|
66
|
Glass-fibre reinforced polyamide based (PA) technopolymer, matte finish.
Black, orange, yellow, red and green colours, matte finish.
Tensile stress: F values reported in the table are the result of breaking tests carried out with the appropriate dynamometric equipment under the test conditions shown in the figure with ambient temperature.